Discover the versatility of earthenware clay with this exclusive pottery bundle! Featuring three premium clay types—PF Red, PM Black, and PA White—this set is perfect for both beginner and seasoned potters. Each clay offers unique color and workability, from the rich red tone of PF, to the deep black finish of PM, to the clean, crisp look of PA. These clays are ideal for hand-building, wheel throwing, and sculpting. Fire to cone 06–04 for stunning results every time. Elevate your pottery projects with this must-try clay bundle!
PA WHITE
TECHNICAL SPECIFICATIONS:
Firing range (biscuit): 1911°-2019°F / Cone 05-03
Water content (throwing): 20%
Plasticity (IP Atterberg): 15
Carbonate content (CaCO3): 17%
Drying shrinkage: 6.2%
Firing shrinkage at Cone 04: -0.2%
Porosity at Cone 04: 12.6%
Dry bending strength: 5.1 N/mm2
Fired bending strength at Cone 04: 27.8 N/mm2
Thermal coefficient (α25-500°C): 74.5x10-7°C-1
Firing range (biscuit): 1050-1080ºC / Cone 05-03
Water content (throwing): 20%
Plasticity (IP Atterberg): 15
Carbonate content (CaCO3): 17%
Drying shrinkage: 6.2%
Firing shrinkage 1050ºC: -0.2%
Porosity (water absorption) 1050ºC: 12.6%
Dry bending strength: 5.1 N/mm2
Fired bending strength 1050ºC: 27.8 N/mm2
Thermal coefficient 1050ºC (25-500ºC): 74.5x10^-7ºC^-1
PF RED
TECHNICAL SPECIFICATIONS:
Firing range: 1855-1971°F / Cone 06-04
Water content (throwing): 22%
Plasticity (IP Atterberg): 17
Carbonate content (CaCO3): 10%
Drying shrinkage: 5.5%
Firing shrinkage at Cone 06: 0.6%
Porosity at Cone 06: 13.5%
Dry bending strength: 6.6 N/mm2
Fired bending strength at Cone 06: 27.9 N/mm2
Thermal coefficient (α25-500°C): 77.7x10-7°C-1
Firing range: 970-1055ºC / Cone 06-04
Water content (throwing): 22%
Plasticity (IP Atterberg): 17
Carbonate content (CaCO3): 10%
Drying shrinkage: 5.5%
Firing shrinkage 1000ºC: 0.6%
Porosity (water absorption) 1000ºC: 13.5%
Dry bending strength: 6.6 N/mm2
Fired bending strength 1000ºC: 27.9 N/mm2
Thermal coefficient 1000ºC (25-500ºC): 77.7x10^-7ºC^-1
PM BLACK
TECHNICAL SPECIFICATIONS:
Firing range: 1911°-2019°F / Cone 06-05
Water content (throwing): 21%
Plasticity (IP Atterberg): 15
Carbonate content (CaCO3): 8%
Drying shrinkage: 5.4%
Firing shrinkage at Cone 04: 0.9%
Porosity at Cone 04: 15.8%
Dry bending strength: 5.3 N/mm2
Fired bending strength at Cone 04: 28.9 N/mm2
Thermal coefficient (α25-500°C): 81.7x10-7°C-1
Firing range: 970-1025ºC / Cone 06-05
Water content (throwing): 21%
Plasticity (IP Atterberg): 15
Carbonate content (CaCO3): 8%
Drying shrinkage: 5.4%
Firing shrinkage 1000ºC: 0.9%
Porosity (water absorption) at 1000ºC: 15.8%
Dry bending strength: 5.3 N/mm2
Fired bending strength 1000ºC: 28.9 N/mm2
Thermal coefficient 1000ºC (25-500ºC): 81.7x10^-7ºC^-1
Storage: Protect ceramic clay bodies from direct sunlight, avoiding excessive temperature changes and protect from frost.
Use: Technical details are available with information on the characteristics of each product and its use. It is recommended to test clay body prior to large scale use in order to verify suitability in both the ceramic process (shaping, drying, firing and decoration) and the final application that is expected to be obtained.
Safety: All SIO-2® clay bodies are certified by the Art & Creative Materials Institute (ACMI) and conform to ASTM D-4236 safety guidelines.
From the manufacturer of SIO-2®:
CERAMICA COLLET S.A.
Always in your hands
Founded in 1874, our company manufactures ceramic clay bodies for industry, pottery and artistic ceramics, and natural clay for crafts, fine arts and education.
Our target is to innovate, developing products made with natural clay which, in many applications, satisfy the high requirements of our customers. Our Quality System, certified according to ISO 9001:2008, is the setting for continuous improvement. Social responsibility, respect, and care for the Environment are two fundamental points in the philosophy of our firm.
The AP Seal identifies art materials that are safe and certified in a toxicological evaluation by a medical expert to contain no materials in sufficient quantities to be toxic or injurious to humans, including children, or to cause acute or chronic health problems. Children in grade six and lower, and adults who may not be able to read and understand safety labeling should use only non-toxic materials. The AP Seal ensures products are non-toxic when used as intended for young children, the physically or mentally handicapped, and any persons who cannot read or understand the safety labeling on product packages.